Method of Concurrently Patterning a Substrate Having a Plurality of Fields and a Plurality of Alignment Marks

ABSTRACT

Imprint lithography templates for patterning substrates are described. The templates include a section having a mold a first pattern of alignment forming areas and template alignment marks. The additional sections are generally devoid of a mold. One or more of the additional section may include the first pattern of a second pattern of alignment forming areas and template alignment marks. The second pattern may correspond to the first pattern.

CROSS-REFERENCE TO RELATED APPLICATION

The present application is a continuation of U.S. patent application Ser. No. 11/695,850 filed Apr. 3, 2007, which claims priority to U.S. provisional application No. 60/788,806 filed on Apr. 3, 2006, both of which are incorporated herein by reference.

BACKGROUND INFORMATION

Nano-fabrication involves the fabrication of very small structures, e.g., having features on the order of nanometers or smaller. One area in which nano-fabrication has had a sizeable impact is in the processing of integrated circuits. As the semiconductor processing industry continues to strive for larger production yields while increasing the circuits per unit area formed on a substrate, nano-fabrication becomes increasingly important. Nano-fabrication provides greater process control while allowing increased reduction of the minimum feature dimension of the structures formed. Other areas of development in which nano-fabrication has been employed include biotechnology, optical technology, mechanical systems and the like.

An exemplary nano-fabrication technique is commonly referred to as imprint lithography. Exemplary imprint lithography processes are described in detail in numerous publications, such as U.S. patent application publication no. 2004/0065976 filed as U.S. patent application Ser. No. 10/264,960; U.S. patent application publication no. 2004/0065252 filed as U.S. patent application Ser. No. 10/264,926; and U.S. Pat. No. 6,936,194, entitled “Functional Patterning Material for Imprint Lithography Processes,” all of which are assigned to the assignee of the present invention.

The imprint lithography technique disclosed in each of the aforementioned U.S. patent application publications and U.S. patent includes formation of a relief pattern in a polymerizable layer and transferring a pattern corresponding to the relief pattern into an underlying substrate. The substrate may be positioned upon a stage to obtain a desired position to facilitate patterning thereof. To that end, a mold is employed spaced-apart from the substrate with a formable liquid present between the mold and the substrate. The liquid is solidified to form a patterned layer that has a pattern recorded therein that is conforming to a shape of the surface of the mold in contact with the liquid. The mold is then separated from the patterned layer such that the mold and the substrate are spaced-apart. The substrate and the patterned layer are then subjected to processes to transfer, into the substrate, a relief image that corresponds to the pattern in the patterned layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a simplified side view of a lithographic system having a template spaced-apart from a substrate;

FIG. 2 is a simplified side view of the substrate shown in FIG. 1, having a patterned layer positioned thereon;

FIG. 3 is a top down view of the template shown in FIG. 1;

FIG. 4 is a flow chart of a method of forming the template shown in FIG. 1;

FIG. 5 is a top down view of a master template formed from e-beam lithography, the master template employed to form template shown in FIG. 1;

FIG. 6 is a top down view of an intermediate substrate formed from the master template shown in FIG. 1; the intermediate substrate having a first field formed and a plurality of substrate alignment marks;

FIG. 7 is a top down view of the substrate alignment marks shown in FIG. 6;

FIG. 8 is a top down view of the master template, shown in FIG. 1, in superimposition with a portion of the intermediate substrate, shown in FIG. 6, with a mesa of the master template being in superimposition with a second field of the intermediate substrate;

FIG. 9 is a top down view of the master template, shown in FIG. 1, in superimposition with a portion of the intermediate substrate, shown in FIG. 6, with a mesa of the master template being in superimposition with a third field of the intermediate substrate;

FIG. 10 is a top down view of the master template, shown in FIG. 1, in superimposition with a portion of the intermediate substrate, shown in FIG. 6, with a mesa of the master template being in superimposition with a fourth field of the intermediate substrate;

FIG. 11 is a top down view of the intermediate substrate, shown in FIG. 6, with a plurality of alignment marks being formed thereon prior to patterning the intermediate substrate; and

FIG. 12 is a top down view of the master template, the master template having 9 fields associated therewith.

DETAILED DESCRIPTION

Referring to FIG. 1, a system 10 to form a relief pattern on a substrate 12 is shown. Substrate 12 may be coupled to a substrate chuck 14. Substrate chuck 14 may be any chuck including, but not limited to, vacuum, pin-type, groove-type, or electromagnetic, as described in U.S. Pat. No. 6,873,087 entitled “High-Precision Orientation Alignment and Gap Control Stages for Imprint Lithography Processes,” which is incorporated herein by reference. In a further embodiment, substrate chuck 14 may be a chuck as described in U.S. Pat. No. 6,982,783 entitled “Chucking System for Modulating Shapes of Substrates” and U.S. Pat. No. 6,980,282 entitled “Method for Modulating Shapes of Substrates”, both of which are incorporated herein by reference. Substrate 12 and substrate chuck 14 may be supported upon a stage 16. Further, stage 16, substrate 12, and substrate chuck 14 may be positioned on a base (not shown). Stage 16 may provide motion along the x and y axes.

Spaced-apart from substrate 12 is a template 18 having a mold 20 extending therefrom towards substrate 20 with a patterning surface 22 thereon. Further, mesa 20 may be referred to as a mold 20. Mesa 20 may also be referred to as a nanoimprint mold 20. In a further embodiment, template 18 may be substantially absent of mold 20. Template 18 and/or mold 20 may be formed from such materials including but not limited to, fused-silica, quartz, silicon, organic polymers, siloxane polymers, borosilicate glass, fluorocarbon polymers, metal, and hardened sapphire. As shown, patterning surface 22 comprises features defined by a plurality of spaced-apart recesses 24 and protrusions 26. However, in a further embodiment, patterning surface 22 may be substantially smooth and/or planar. Patterning surface 20 may define an original pattern that forms the basis of a pattern to be formed on substrate 12.

Template 18 may be coupled to a template chuck 28, template chuck 28 being any chuck including, but not limited to, vacuum, pin-type, groove-type, or electromagnetic, as described in U.S. Pat. No. 6,873,087. In a further embodiment, substrate chuck 14 may be a chuck as described in U.S. Pat. No. 6,982,783 and U.S. Pat. No. 6,980,282. Template chuck 28 may be coupled to an imprint head 30 to facilitate movement of template 18 and mold 20.

System 10 further comprises a fluid dispense system 32. Fluid dispense system 32 may be in fluid communication with substrate 12 so as to deposit a polymeric material 34 thereon. System 10 may comprise any number of fluid dispensers and fluid dispense system 32 may comprise a plurality of dispensing units therein. Polymeric material 34 may be positioned upon substrate 12 using any known technique, e.g., drop dispense, spin-coating, dip coating, chemical vapor deposition (CVD), physical vapor deposition (PVD), thin film deposition, thick film deposition, and the like. As shown, polymeric material 34 may be deposited upon substrate 12 as a plurality of spaced-apart droplets 36. Typically, polymeric material 34 is disposed upon substrate 12 before the desired volume is defined between mold 20 and substrate 12. However, polymeric material 34 may fill the volume after the desired volume has been obtained.

Referring to FIGS. 1 and 2, system 10 further comprises a source 38 of energy 40 coupled to direct energy 40 along a path 42. Imprint head 30 and stage 16 are configured to arrange mold 20 and substrate 12, respectively, to be in superimposition and disposed in path 42. Either imprint head 30, stage 16, or both vary a distance between mold 20 and substrate 12 to define a desired volume therebetween such that mold 20 contacts polymeric material 34 and the desired volume is filled by polymeric material 34. More specifically, polymeric material 34 of droplets 36 may ingress and fill recesses 24 of mold 20. After the desired volume is filled with polymeric material 34, source 38 produces energy 40, e.g., broadband ultraviolet radiation that causes polymeric material 34 to solidify and/or cross-link conforming to the shape of a surface 44 of substrate 12 and patterning surface 22, defining a patterned layer 46 on substrate 12. Patterned layer 46 may comprise a residual layer 48 and a plurality of features shown as protrusions 50 and recessions 52.

System 10 may further comprise an actuation system 58 surrounding template 18/mold 20 to facilitate alignment and overlay registration between mold 20 and substrate 12. Actuation system 58 facilitates alignment and overlay registration by selectively deforming template 18/mold 20. This facilitates correcting various parameters of the pattern shape, i.e., magnification characteristics, skew/orthogonality characteristics, and trapezoidal characteristics. An example of an actuation system 58 is described in U.S. Pat. No. 7,150,622 entitled “Systems for Magnification and Distortion Correction for Imprint Lithography Processes”; U.S. Pat. No. 7,170,589 entitled “Apparatus to Vary Dimensions of a Substrate During Nano-Scale Manufacturing”; and U.S. Pat. No. 6,916,585 entitled “Method of Varying Template Dimensions to Achieve Alignment During Imprint Lithography”; all of which are incorporated by reference herein.

System 10 may be regulated by a processor 54 that is in data communication with stage 16, imprint head 30, fluid dispense system 32, source 38, and actuation system 58 operating on a computer readable program stored in memory 56.

Referring to FIG. 3, a top down view of template 18 is shown. More specifically, mold 20 of template 18 is shown comprising a plurality of dies 60, shown as dies 60 a-60 d. However, in a further embodiment, mold 20 may comprise any number of dies, i.e., 2, 4, 6, 8, or 9 dies. Furthermore, each of dies 60 a-60 d may have substantially the same relief structure 61 formed therein. To that end, formation of dies 60 of mold 20 may be formed employing e-beam lithography. However, employing e-beam lithography may result in, inter alia, increased formation time of template 18, which may be undesirable. To that end, a method of minimizing formation time of dies 60 of mold 20 is described below.

Referring to FIGS. 3-5, in a first embodiment, a method of forming dies 60 of mold 20 is shown. More specifically at step 100, a master template 62 may be formed employing e-beam lithography. Master template 62 comprises a plurality of sections 64, shown as sections 64 a-64 d. However, in a further embodiment, master template 62 may comprise any number of sections 64, i.e., 2, 4, 6, 8, or 9 sections. Each section of sections 64 may be separated from an adjacent section of sections 64 by a street 66. Further, each of sections 64 may be separated from a perimeter 68 of master template 62 by a street 70.

A section of sections 64 may comprises a mesa 72 having a relief pattern 74 defined therein. As shown, mesa 72 may be positioned in section 64 a, however, in a further embodiment, mesa 72 may be positioned in any section of sections 64. Mesa 72 comprises sides 76 a, 76 b, 76 c, and 76 d, with side 76 a being positioned opposite to side 76 c and side 76 b being positioned opposite to side 76 d. In an example, master template 62 may have a thickness of equal to or greater than 4 mm.

Master template 62 may further comprise a plurality of alignment forming areas 78 and template alignment marks 80. Alignment forming areas 78 and template alignment marks 80 may be positioned within streets 66 and 70. In a further embodiment, alignment forming areas 78 and template alignment marks 80 may be positioned on a plurality of mesas. In still a further embodiment, alignment forming areas 78 may comprise checkerboard forming alignment marks and template alignment marks 80 may comprise grating alignment marks. In still a further embodiment, template alignment marks 80 may be substantially planar.

Positioned adjacent mesa 72 are a first subset of alignment forming areas 78 and template alignment marks 80 defining a first pattern 82 a. As shown, positioned proximate each of sides 76 a, 76 b, 76 c, and 76 d are two alignment forming areas 78 and two template alignment marks 80. However, in a further embodiment, any number of alignment forming areas 78 and template alignment marks 80 may be positioned proximate sides 76 a, 76 b, 76 c, and 76 d.

Master template 62 may further comprise alignment forming areas 78 and template alignment marks 80 positioned in streets 66 and 70 proximate to the remaining sections 64 of master template 62. More specifically, a second, third, and fourth subsets of alignment forming areas 78 and template alignment marks 80 may be positioned in streets 66 and 70 proximate to sections 64 b, 64 c, and 64 d, respectively, defining a second pattern 82 b, a third pattern 82 c, and a fourth pattern 82 d, respectively. The first pattern 82 a may be substantially the same as the third pattern 82 c and the second pattern 82 b may be substantially the same as the fourth pattern 82 d. Further, the first and third patterns 82 a and 82 c may be differ from the second and fourth patterns 82 b and 82 d.

Referring to FIGS. 4-6, at step 102, polymeric material 34 may be positioned on a intermediate substrate 84 by drop dispense, spin-coating, dip coating, chemical vapor deposition (CVD), physical vapor deposition (PVD), thin film deposition, thick film deposition, and the like. More specifically, intermediate substrate 84 may comprise a plurality of fields 86, shown as fields 86 a-86 d. However, in a further embodiment, intermediate substrate 84 may comprises any number of fields 86, i.e. 2, 4, 6, 8, or 9 fields. In the present example, the number of fields 86 of intermediate substrate 84 may be substantially the same as the number of sections 64 of mater template 62. To that end, polymeric material 34 may be positioned on field 586 a. Furthermore, polymeric material 34 may be positioned on a plurality of regions 88, with regions laying 88 outside of fields 86 a-86 d. In an example, intermediate substrate 84 may have a thickness of in a range of 0.05 mm to 3 mm.

At step 104, a desired spatial relationship may be obtained between master template 62 and intermediate substrate 84, and more specifically, between field 86 a and mesa 72. Further at step 104, polymeric material 34 of field 86 a may fill the desired volume between field 86 a of intermediate substrate 84 and mesa 72 of master template 62 and polymeric material 34 of regions 88 may fill the desired volume between regions 88 of substrate and alignment forming areas 78 of master template 62.

At step 106, polymeric material 34 positioned on field 86 a and regions 88 of intermediate substrate 84 may be solidified and/or cross-linked and mesa 72 of master template 62 may be separated from polymeric material 34 positioned on field 86 a, defining a patterned layer 90 a, and may be separated from polymeric material 34 positioned on regions 88, defining substrate alignment marks 92. As a result of intermediate substrate 84 having a thickness substantially less than a thickness of master template 62, a separation force may be minimized, which may be desirable.

Referring to FIG. 7, in a further embodiment, each of substrate alignment marks 92 may further comprise image placement metrology marks 94. Image placement metrology marks 94 may be measured known image placement or image registration systems, e.g., LMS IPRO available from Leica Microsystems of Bannockburn, Ill.

Referring to FIGS. 4, 5, and 8, at step 108, polymeric material 34 may be positioned on field 86 b in any of the methods mentioned above with respect to FIG. 6 and step 102.

At step 110, a desired spatial relationship may be obtained between template alignment marks 80 of master template 62 and substrate alignment marks 92 of intermediate substrate 84 such that a desired spatial relationship between master template 62 and intermediate substrate 84 may be obtained, and more specifically, in the present example, between field 86 b and mesa 72. A desired spatial relationship between template alignment marks 80 and substrate alignment marks 92 may include template alignment marks 80 and substrate alignment marks 92 being in superimposition; however, in a further embodiment, template alignment marks 80 and substrate alignment marks 92 may be offset in the x-y plane a desired amount to compensate for variations among the first, second, third, and fourth patterns 82 a, 82 b, 82 c, and 82 d of alignment forming areas 78 and template alignment marks 80.

Alignment between template alignment marks 80 and substrate alignment marks 92 may be determined employing an alignment system as described in U.S. Pat. No. 7,292,326 entitled “Interferometric Analysis for the Manufacture of Nano-Scale Devices,” which is incorporated herein by reference. Further at step 110, polymeric material 34 of field 86 b may fill the desired volume between field 86 b of intermediate substrate 84 and mesa 72 of master template 62.

At step 112, polymeric material 34 positioned on field 86 b of intermediate substrate 84 may be solidified and/or cross-linked and mesa 72 of master template 62 may be separated from polymeric material 34 positioned on intermediate substrate 84, defining a patterned layer 90 b on field 86 b.

Referring to FIGS. 4, 5, and 9, at step 114, polymeric material 34 may be positioned on field 86 c in any of the methods mentioned above with respect to FIG. 6 and step 102.

At step 116, a desired spatial relationship may be obtained between template alignment marks 80 of master template 62 and substrate alignment marks 92 of intermediate substrate 84 such that a desired spatial relationship between master template 62 and intermediate substrate 84 may be obtained, and more specifically, in the present example, between field 86 c and mesa 72. To that end, to obtain a desired spatial relationship between template alignment marks 80 of master template 62 and substrate alignment marks 92, master template 62 may be rotated about the z-axis, and more specifically, rotated 180° with respect to intermediate substrate 84. As a result, a desired spatial relationship may be obtained between template alignment marks 80 and substrate alignment marks 92. Further at step 116, polymeric material 34 of field 86 c may fill the desired volume between field 86 c of intermediate substrate 84 and mesa 72 of master template 62. In a further embodiment, master template 62 may be rotated prior to positioning polymeric material 34 on fields 86 c of intermediate substrate 84.

At step 118, polymeric material 34 positioned on field 86 c of intermediate substrate 84 may be solidified and/or cross-linked and mesa 72 of master template 62 may be separated from polymeric material 34 positioned on field 86 a, defining a patterned layer 90 c.

Referring to FIGS. 4 and 5, at step 120, steps 108, 110, and 112 may be repeated for field 86 d of intermediate substrate 84, defining patterned layer 90 d on field 86 d. In a further embodiment, steps 108, 110, and 112 may be repeated for any number of fields 86 of intermediate substrate 84.

Referring to FIGS. 4, 5, and 10, after forming patterned layers 90 a, 90 b, 90 c, and 90 d on fields 86 a, 86 b, 86 c, and 86 d, respectively, intermediate substrate 84 may be employed to form a pattern in a final substrate 96. More specifically, at step 122, polymeric material 34 may be positioned on final substrate 96 employing any of the methods mentioned above with respect to step 102 and FIG. 6. Final substrate 96 may comprise a plurality of fields 98, shown as fields 98 a-98 d. However, in a further embodiment, final substrate 96 may comprises any number of fields 98, i.e. 2, 4, 6, 8, or 9 fields. In the present embodiment, the number of fields 98 of final substrate 96 may be substantially the same as the number of fields 86 of intermediate substrate 84. To that end, polymeric material 34 may be positioned on fields 98 of final substrate 96. In an example, final substrate 96 may have a thickness of equal to or greater than 4 mm.

At step 124, a desired spatial relationship may be obtained between intermediate substrate 84 and final substrate 96 such that polymeric material 34 on final substrate 96 may fill the desired volume between intermediate substrate 84 and final substrate 96.

At step 126, polymeric material 34 positioned on final substrate 96 may be solidified and/or cross-linked and intermediate substrate 84 may be separated from polymeric material 34 positioned on final substrate 96, defining a plurality of patterned layers 99 in each of fields 98, with each of patterned layers 99 being substantially the same as dies 60 of mold 20, and thus, final substrate 96 may be substantially the same as template 18.

Referring to FIGS. 4-6, in a second embodiment, it may be desired to form template 18 from master template 62 in a single patterning step. To that end, each of patterned layer 90 positioned on fields 86 of intermediate substrate 84 may be substantially the same as dies 60 of mold 20 and thus, intermediate substrate 84 may be substantially the same as template 18. In the present example, master template 62 may have a thickness of approximately 2.29 mm and intermediate substrate 84 may have a thickness of 6.35 mm.

Referring to FIG. 11, in still a further embodiment, substrate alignment marks 92 may be formed on intermediate substrate 84 in a separate step. More specifically, substrate alignment marks 92 may be formed on intermediate substrate 84 prior to forming patterned layer 90 on intermediate substrate 84. To that end, substrate alignment marks 92 may be formed employing a) an optical lithography tool with accurate global inteferometry, such as a 913 nm scanner lithography tool available from ASML of the Netherlands or b) an optical lithography tool with excel interferometry, such as the Nanoruler described at http://www.sciencedaily.com/releases/2004/02/040203233840.htm, which is incorporated herein by reference. As a result, alignment between fields 86 of intermediate substrate 84 may be obtained, i.e., field to field alignment.

Referring to FIGS. 3, 5, and 6, to that end, as described above, mold 20 may have four dies associated therewith. However, as mentioned above, mold 20 may have any number of dies associated therewith, and thus, master template 62, intermediate substrate 84, and final substrate 96 may scale according. As shown in FIG. 12, master template 62 may have nine sections 64 associated therewith. To that end, each of sections 64 of master template 62 may have a pattern of alignment forming areas 78 and template alignment marks 80 proximate thereto, and more specifically, each section of sections 64 may have a pattern of alignment forming areas 78 and template alignment marks 80 differing from a pattern of alignment forming areas 78 and template alignment marks 80 of surrounding sections of sections 64. More specifically, sections 64 a, 64 c, 64 e, 64 g, and 64 i may have a fifth pattern of alignment forming areas 78 and template alignment marks 80 proximate thereto and sections 64 b, 64 d, 64 f, and 64 h may have a sixth pattern of alignment forming areas 78 and template alignment marks 80 proximate thereto, with the fifth pattern of alignment forming areas 78 and template alignment marks 80 being substantially the same as the first pattern mentioned above with respect to FIG. 5, and the sixth pattern of alignment forming areas 78 and template alignment marks 80 being substantially the same as the third pattern mentioned above with respect to FIG. 5. Further, each of sections 64 e, 64 g, and 64 i may be patterned in the above-mentioned method analogous to patterning of section 64 c and each of sections 64 f and 64 h may be patterned in the above-mentioned method analogous to patterning of sections 64 b and 64 d.

Furthermore, it may be desired to minimize mechanical distortions present in template 18 formed in any of the methods mentioned above. To that end, master template 62, intermediate substrate 84, and final substrate 96 may be substantially flat. More specifically, master template 62, intermediate substrate 84, and final substrate 96 may have a flatness better than 100 nm, preferably better than 50 nm, preferably better than 20 nm and further preferably better than 10 nm over the patterning area. To further minimize the aforementioned mechanical distortions, inter alia, minimize image placement errors, intermediate substrate 84 may conform to master template 62. To that end, master template 62, intermediate substrate 84, and final substrate 96 may be positioned upon a chuck analogous to substrate chuck 14 mentioned above with respect to FIG. 1. To that end, a shape of master template 62, intermediate substrate 84, and final substrate 96 may be determined employing an air gauge system (not shown) coupled with an XY stage (not shown); a laser distance sensor system (not shown) coupled with an XY stage (not shown); or a full field 3D profiler (not shown) as described in http://www.zygo.com/?/products/metrology.htm, which is incorporated by reference herein. Moreover, each of master template 62, intermediate substrate 84, and final substrate 96 may be formed from substantially the same material, with the material including but not limited to, fused-silica and ultra-low-expansion glass. Further, a difference in temperature between master template 62, intermediate substrate 84, and final substrate 96 may be less than 0.05° C., preferably less than 0.01° C., and further preferably less than 0.001° C.

To further minimize, if not prevent, errors present formed in any of the methods mentioned above, in the first embodiment mentioned above, master template 62 may have an actuation system coupled thereto analogous to actuation system 58 mentioned above with respect to FIG. 1. In the second embodiment mentioned above, final substrate 96 may have an actuation system coupled thereto analogous to actuation system 58 mentioned above with respect to FIG. 1.

The above-mentioned methods may be analogously employed in formation of photomasks for photolithography. Photomasks are typically 4× (the relief pattern of the photomask is 5 times the size of the desired features to be formed on the substrate). Advanced photomask that may be employed in photolithography with KrF (248 nm) laser and ArF (193 nm) laser may further comprise sub-resolution features that are smaller than the primary features. These sub-resolution features may be also known as optical proximity correction features or reticle enhanced features. The sub-resolution features do not print; they are designed to enhance the quality of the primary features. As mentioned above, the primary features are 4×. For example, for a feature of the size of 50 nm on the wafer, the primary photomask feature is 200 nm. The sub-resolution features may be as small as 1× or smaller or as large as approaching 4×. Typically the small sub-resolution features are about 1.5×; for 50 nm wafer features, this translates to 75 nm on the photomask. The 4× photomasks are for example are of size 100 mm by 100 mm for a 25 mm by 35 mm wafer field size; and 104 mm by 132 mm for a 26 mm by 33 mm wafer field size. These fields typically have 2, 4, 6, or more dies in them each of which have substantially the same pattern requirements. Thus, the above-mentioned method may be analogously employed in formation of photomasks for photolithography.

The embodiments of the present invention described above are exemplary. Many changes and modifications may be made to the disclosure recited above, while remaining within the scope of the invention. Therefore, the scope of the invention should not be limited by the above description, but instead should be determined with reference to the appended claims along with their full scope of equivalents. 

1. A nano imprint lithography template, comprising: a plurality of sections including: a first section having a mold and a first subset of alignment forming areas and a plurality of template alignment marks defining a first pattern; and a second section having a second subset of alignment forming areas and a plurality of template alignment marks defining a second pattern; wherein the first pattern corresponds to the second pattern.
 2. The nano imprint lithography template of claim 1, wherein the second section is devoid of a mold.
 3. The nano imprint lithography template of claim 1, wherein the alignment forming areas are checkerboard forming alignment marks and the template alignment marks are grating alignment marks.
 4. The template of claim 1, wherein the alignment forming areas are checkerboard forming alignment marks and the template alignment marks are substantially planar.
 5. A nano imprint lithography template, comprising: a first section having a first dimension of a length and a width, the first section having a mold with a relief pattern; and, a second section having second dimensions of a length and a width, the second section devoid of a mold, wherein the first dimensions are substantially similar to the second dimensions.
 6. The nano imprint lithography template of claim 5, further comprising a first pattern of alignment forming areas and template alignment marks positioned adjacent to the first section.
 7. The nano imprint lithography template of claim 6, further comprising a second pattern of alignment forming areas and template alignment marks positioned adjacent to the second section, wherein the first pattern is different from the second pattern.
 8. A nano imprint lithography template, comprising: a plurality of sections, each section having substantially similar dimensions of length and width, with only one of the plurality of sections having a mold, the mold having a relief pattern defined therein.
 9. The template of claim 8, further comprising a plurality of alignment forming areas and template alignment marks.
 10. The template of claim 9, wherein each section is separated from each adjacent section by a street and each section is separated from the perimeter of the template by a street and the plurality of alignment forming areas and template alignment marks are positioned within the streets.
 11. The template of claim 10, wherein the alignment forming areas are checkerboard forming alignment marks and the template alignment marks are grating alignment marks.
 12. The template of claim 10, wherein the alignment forming areas are checkerboard forming alignment marks and the template alignment marks are substantially planar.
 13. The template of claim 8, further comprising a first subset of alignment forming areas and a first subset of template alignment marks defining a first pattern positioned adjacent to the mold.
 14. The template of claim 13, further comprising a second subset of alignment forming areas and a second subset of template alignment marks defining a second pattern, wherein the second pattern corresponds to the first pattern. 